Al₂0₃-Ti0₂ Alumina titanium oxide 80/20 ceramic powder

Item No.: PZ-AT20
Al₂0₃-Ti0₂
Alumina titanium oxide 80/20 ceramic powder
Melt broken
Reunion sintering
INQUIRY
Description
 
 Type of powder material
 Al₂0₃-Ti0₂   Alumina titanium oxide 80/20 ceramic powder    Melt broken     Reunion sintering
 brand (PZ)
 PZ-AT20
 specifications(um) 
 30/10      45/15      90/45
 Performance and application
 The APS,
 The maximum operating temperature 540 ℃
 corrosion resistance, wear resistance, sliding wear resistance
 it is typically used as the guiding part of thread ends in textile machinery with hardness lower than AT13


Typical chemical composition
 
Al₂0₃ base
Si0₂ < 0.5%
Ti0₂ - 13.0%
Fe₂0₃ < 0.2%
Mg0 < 0.1%
Ca0 < 0.1%


Spray parameters
 
 Plasmagenerator   F4 
Plasma Gas Ar(SLPM) 40
Plasma Gas H₂(SLPM) 14
Current(A) 550
Spray Distnce(mm) 120

                                                                                                                                                                                    

The coating performance

Hardness: approx. 1000 HV 0,3        Applicable up to 550 °C        Good Grinding and Polishing Properties


The product application
 
Thread guide
Part function:Yarn tension compensation
Matrix material:aluminum
Coating function:Form abrasion resistant coating with specific roughness to optimize yarn guidance
Process technology:Atmospheric plasma spraying

 