Al₂0₃-Ti0₂ Alumina titanium oxider 60/40 ceramic powde

Item No.: PZ-AT40
Al₂0₃-Ti0₂
Alumina titanium oxide 60/40 ceramic powder
Melt broken
Reunion sintering
INQUIRY
Description
 
 Type of powder material
 Al₂0₃-Ti0₂    Alumina titanium oxide 60/40 ceramic powder   Melt broken   Reunion sintering
 brand (PZ)
 PZ-AT40
 specifications(um)
 30/10     45/15     90/45
 Performance and application

 The APS,

 The maximum operating temperature 540 ℃

  hardness is lower than AT13 and AT20

  wear resistance, corrosion resistance, poor chemical resistance, easy to grind, high finish coating

  used in textile industry, household equipment (such as pan), etc



Typical chemical composition
 
Al₂0₃ base
Si0₂ <0.5%
Ti0₂ ~ 40.0%
Fe₂0₃ < 0.4%
Mg0 < 0.2%
Ca0 < 0.1%



Spray parameters
 
 Plasmagenerator   F4 
Plasma Gas Ar(SLPM) 43
Plasma Gas H₂(SLPM) 14
Current(A) 580
Spray Distnce(mm) 120

                                                                                                                                                                                    
Coating Properties

Hardness:approx.1.000 HV 0.3          Applicable up to 540℃          Good Grinding and polishing properties


The product application
 
roll Thread guide
Part function: Guide and draw the yarn Part function: Yarn tension compensation
Matrix material:Steel or aluminum Part function: Yarn tension compensation
Coating function:Form abrasion resistant coating with specific roughness to optimize yarn guidance  Coating function:Form abrasion resistant coating with specific roughness to optimize yarn guidance
Process technology:Plasma spraying
Process technology: Atmospheric plasma spraying