Al₂0₃-Ti0₂ Alumina titanium oxider 87/13 ceramic powde

Item No.: PZ-AT13
Al₂0₃-Ti0₂
Alumina titanium oxider 87/13 ceramic powde
Melt broken
Reunion sintering
INQUIRY
Description
 
 Type of powder material
 Al₂0₃-Ti0₂ Alumina titanium oxider 87/13 ceramic powde     Melt broken    Reunion sintering
 brand(PZ)
 PZ-AT13
 specifications(um)
 30/10      45/15      90/45
 Performance and application

 The APS

 The maximum operating temperature 540 ℃

 hardness is lower than AT13 and AT20

 wear resistance, corrosion resistance, poor chemical resistance, easy to grind, high finish coating

 used in textile industry, household equipment (such as pan), etc



Typical chemical composition
 
Al₂0₃ base
Si0₂ < 0.5%
Ti0₂ ~ 13.0%
Fe₂0₃ < 0.2%
Mg0 < 0.1%
Ca0 < 0.1%


Spray parameters
 
 Plasmagenerator   F4 
Plasma Gas Ar(SLPM) 40
Plasma Gas H₂(SLPM) 14
Current(A) 550
Spray Distnce(mm) 120

                                                                                                                                                                                    

The coating performance

Hardness: approx. 1000 HV 0,3              Applicable up to 550 °C                Good Grinding and Polishing Properties


The product application
 
Thread guide roll
Part function:Yarn tension compensation Part function: Guide and draw the yarn
Matrix material:aluminum Matrix material:Steel or aluminum
Coating function:Form abrasion resistant coating with specific roughness to optimize yarn guidance Coating function:Form abrasion resistant coating with specific roughness to optimize yarn guidance
Process technology:Atmospheric plasma spraying
Process technology:Plasma spraying