| Type of powder material |
| Al₂0₃-Ti0₂ Alumina titanium oxide 60/40 ceramic powder Melt broken Reunion sintering |
| brand (PZ) |
| PZ-AT40 |
| specifications(um) |
| 30/10 45/15 90/45 |
| Performance and application |
|
The APS, The maximum operating temperature 540 ℃ hardness is lower than AT13 and AT20 wear resistance, corrosion resistance, poor chemical resistance, easy to grind, high finish coating used in textile industry, household equipment (such as pan), etc |
| Al₂0₃ | base |
| Si0₂ | <0.5% |
| Ti0₂ | ~ 40.0% |
| Fe₂0₃ | < 0.4% |
| Mg0 | < 0.2% |
| Ca0 | < 0.1% |
| Plasmagenerator | F4 |
| Plasma Gas Ar(SLPM) | 43 |
| Plasma Gas H₂(SLPM) | 14 |
| Current(A) | 580 |
| Spray Distnce(mm) | 120 |
| roll | Thread guide |
| Part function: Guide and draw the yarn | Part function: Yarn tension compensation |
| Matrix material:Steel or aluminum | Part function: Yarn tension compensation |
| Coating function:Form abrasion resistant coating with specific roughness to optimize yarn guidance | Coating function:Form abrasion resistant coating with specific roughness to optimize yarn guidance |
Process technology:Plasma spraying |
Process technology: Atmospheric plasma spraying |